peel ply, release fabric

release fabric: 1.white color with red stripe 2.blade separation and Cabin cover; 3.free of oil and other release agents;

DESCRIPTION:

Peel Ply fabrics may be used to build large composite structures or to facilitate small repairs where a clean, textured surface is desired for additional bonding and finishing operations. A Peel Ply layer also provides pressure to the GRP composite structure during fabrication and cure allowing gas to escape thereby eliminating blisters. Where Peel Ply fabric is used, the laminate will be smoother and will achieve a higher fiber to resin content thus increasing strength. Without Peel Ply, production of vacuum-formed laminates, especially composites made with epoxy/carbon/Kevlar, is hardly possible. Furthermore, excellent non-skid surfaces can be obtained.

The peel ply material is generally used to allow the builder to have a "re-bondable" surface which requires no additional preparation once the peel ply is removed. That is very important, however, the peel ply serves other important functions as well. When applied over the wet lay-ups, you have a surface that will allow you to squeegee trapped air out without allowing the glass layers to move and shift around .  When the resin/fiberglass layup is cured and the peel ply is removed, the surface will be free of harmful sharp edges and spurs.

Note: If you do have the sticky surface because the resin was applied without peel ply, wash the surface with a clean rag soaked with acetone. The acetone will remove the uncured resin and allow load free sanding.

SPECIFICATION:

Weight	density	color	thickness(mm)	tensile strength(N)	temperature resistant (°C)
85g/m2	17*16	white with red stripes	0.016	270N	200

peel ply, release fabric